Properties of Ni and Ni–Fe nanowires electrochemically deposited into a porous alumina template

• Alla I. Vorobjova,
• Dmitry L. Shimanovich,
• Kazimir I. Yanushkevich,
• Sergej L. Prischepa and
• Elena A. Outkina

Beilstein J. Nanotechnol. 2016, 7, 1709–1717, doi:10.3762/bjnano.7.163

• value of Ni–Fe NWs in the alumina template is higher than that of the Ni sample and bulk Ni, also the Curie temperature of the Ni–Fe sample (790 K) is higher than that of the Ni sample one or bulk Ni. Keywords: electrochemical deposition; nanowire; porous alumina template; specific magnetization

• heights is presented. The structural properties of PA/Ni and PA/Ni–Fe NWs, as well as the temperature dependence of the specific magnetization of these nanocomposites are investigated and discussed. Experimental Preparation of porous alumina template The preparation technique and the thickness of the PA

• that of the Ni sample and bulk Ni, and is equal to 790 K, which is rather high. Note, that this value is less than the Tc of bulk Fe (1040 K) and Py (823 K) [47]. Conclusion Arrays of compact Ni–Fe NWs with high aspect ratio (about 500) and diameters of 50 nm have been fabricated using a porous alumina